Elidron 201

Elidron 201 releases Nitrogen gas which is useful for washing and degassing the molten alloy. Nitrogen gas removes hydrogen entrapped by the metal during melting operations and brings to bath surface all oxides, micro-oxides and impurities. Elidron 201 tablets have a combined effect. The tablets, dissolved by metal temperature, release nitrogen gas capable to remove … Continued

Aluxal 267

High quality flux, in powder form, for sodium addition into Al-Si alloys with silicon content ranging between 7-13%. Modification treatment alters the silicon structure of the alloy and improves castings mechanical properties. The silicon structure changes from coarse, angular, acicular crystals into fine, rounded, interconnected fibrous particles, perfectly distributed in the aluminium matrix. The main … Continued

Flotab 5

In gravity and sand foundries, eutectic aluminium silicon alloys (Silicon 7-13%) should normally be treated with sodium fluxes to modify the silicon structure and improve mechanical characteristics. After treating the alloys with products such as Crystal 2007/M, Napal 700 or Nabox: it is important to use Flotab 5 to keep the desired amount of sodium … Continued

Crystal 2007/M

High quality flux, in granular form, for sodium addition into Al-Si alloys with silicon content ranging between 7-13%. Modification treatment alters the silicon structure of the alloy and improves castings mechanical properties. The silicon structure changes from coarse, angular, acicular crystals into fine, rounded, interconnected fibrous particles, perfectly distributed in the aluminium matrix. The main … Continued

AlTiB

Aluminium Titanium 5% Boron 1% is a solid metal rod, available in cutted rod or coils, used in aluminium cast-houses foundries or billets casting plants to aid nucleation and grain refining of aluminium alloys. AlTiB must be added in the liquid aluminium alloys at temperatures ranging from 680 up to 780°C. The alloy degassing will … Continued

Germinal 1604

Germinal 1604 is a high yield grain refining flux in tablet form. It is sodium free and contains high quantity of Titanium and Boron to allow a fine grain formation in the structure of Aluminium-Magnesium alloys. The product doesn’t have degassing action, therefore it is advisable to use degassing flux after the treatment with Germinal … Continued

Aluxal 203 SS FPS

ALUXAL 203 SS F.P.S. is flux studied for covering and drossing-off treatments of aluminium alloys. The flux creates a physical barrier between molten aluminium and furnace atmosphere during the melting. The product reduces oxides inclusion and allows the production of high quality casting. The dross produced during the exothermic reaction is dry and very low … Continued