Crystal 2600 7 August 2017 By anna Crystal 2600 is produced in granular form and has an improved formulation to perform effective covering and drossing on molten aluminium alloys. The product is normally recommended for melts standing in melting furnace, in transport ladles or during rotor degassing in ladles and crucibles. The formulation is based on inorganic and natural blended salts. This … Continued
Flotab 10 7 August 2017 By anna Flotab 10 tablets are recommended for a cleaning and deoxidising action over molten aluminium alloys contained in reverberatory furnaces (over 5 tons capacity). This product has been especially formulated to obtain an effective reduction in the formation of oxides and drosses that normally adhere on refractory walls. Flotab 10 avoids the risk of hard inclusions … Continued
Elidron 201 7 August 2017 By anna Elidron 201 releases Nitrogen gas which is useful for washing and degassing the molten alloy. Nitrogen gas removes hydrogen entrapped by the metal during melting operations and brings to bath surface all oxides, micro-oxides and impurities. Elidron 201 tablets have a combined effect. The tablets, dissolved by metal temperature, release nitrogen gas capable to remove … Continued
Aluxal 267 7 August 2017 By anna High quality flux, in powder form, for sodium addition into Al-Si alloys with silicon content ranging between 7-13%. Modification treatment alters the silicon structure of the alloy and improves castings mechanical properties. The silicon structure changes from coarse, angular, acicular crystals into fine, rounded, interconnected fibrous particles, perfectly distributed in the aluminium matrix. The main … Continued
Flotab 5 7 August 2017 By anna In gravity and sand foundries, eutectic aluminium silicon alloys (Silicon 7-13%) should normally be treated with sodium fluxes to modify the silicon structure and improve mechanical characteristics. After treating the alloys with products such as Crystal 2007/M, Napal 700 or Nabox: it is important to use Flotab 5 to keep the desired amount of sodium … Continued
Crystal 2007/M 7 August 2017 By anna High quality flux, in granular form, for sodium addition into Al-Si alloys with silicon content ranging between 7-13%. Modification treatment alters the silicon structure of the alloy and improves castings mechanical properties. The silicon structure changes from coarse, angular, acicular crystals into fine, rounded, interconnected fibrous particles, perfectly distributed in the aluminium matrix. The main … Continued
AlTiB 7 August 2017 By anna Aluminium Titanium 5% Boron 1% is a solid metal rod, available in cutted rod or coils, used in aluminium cast-houses foundries or billets casting plants to aid nucleation and grain refining of aluminium alloys. AlTiB must be added in the liquid aluminium alloys at temperatures ranging from 680 up to 780°C. The alloy degassing will … Continued
Crystal 2000 7 August 2017 By anna Covering and drossing-off flux characterized by the absence of toxic and harmful chemicals, complete absence of dust and very low employment rate. Crystal 2000 overcomes the problems associated with the traditional powder fluxes by making handling and charging easier and safer. Also eliminates losses from furnace emissions. As result, dosage is reduced and foundry environment … Continued