Crystal 2600

Crystal 2600 is produced in granular form and has an improved formulation to perform effective covering and drossing on molten aluminium alloys. The product is normally recommended for melts standing in melting furnace, in transport ladles or during rotor degassing in ladles and crucibles. The formulation is based on inorganic and natural blended salts. This … Continued

Flotab 10

Flotab 10 tablets are recommended for a cleaning and deoxidising action over molten aluminium alloys contained in reverberatory furnaces (over 5 tons capacity). This product has been especially formulated to obtain an effective reduction in the formation of oxides and drosses that normally adhere on refractory walls. Flotab 10 avoids the risk of hard inclusions … Continued

Elidron 201

Elidron 201 releases Nitrogen gas which is useful for washing and degassing the molten alloy. Nitrogen gas removes hydrogen entrapped by the metal during melting operations and brings to bath surface all oxides, micro-oxides and impurities. Elidron 201 tablets have a combined effect. The tablets, dissolved by metal temperature, release nitrogen gas capable to remove … Continued

Aluxal 267

High quality flux, in powder form, for sodium addition into Al-Si alloys with silicon content ranging between 7-13%. Modification treatment alters the silicon structure of the alloy and improves castings mechanical properties. The silicon structure changes from coarse, angular, acicular crystals into fine, rounded, interconnected fibrous particles, perfectly distributed in the aluminium matrix. The main … Continued

Flotab 5

In gravity and sand foundries, eutectic aluminium silicon alloys (Silicon 7-13%) should normally be treated with sodium fluxes to modify the silicon structure and improve mechanical characteristics. After treating the alloys with products such as Crystal 2007/M, Napal 700 or Nabox: it is important to use Flotab 5 to keep the desired amount of sodium … Continued

Crystal 2007/M

High quality flux, in granular form, for sodium addition into Al-Si alloys with silicon content ranging between 7-13%. Modification treatment alters the silicon structure of the alloy and improves castings mechanical properties. The silicon structure changes from coarse, angular, acicular crystals into fine, rounded, interconnected fibrous particles, perfectly distributed in the aluminium matrix. The main … Continued

AlTiB

Aluminium Titanium 5% Boron 1% is a solid metal rod, available in cutted rod or coils, used in aluminium cast-houses foundries or billets casting plants to aid nucleation and grain refining of aluminium alloys. AlTiB must be added in the liquid aluminium alloys at temperatures ranging from 680 up to 780°C. The alloy degassing will … Continued

Crystal 2000

Covering and drossing-off flux characterized by the absence of toxic and harmful chemicals, complete absence of dust and very low employment rate. Crystal 2000 overcomes the problems associated with the traditional powder fluxes by making handling and charging easier and safer. Also eliminates losses from furnace emissions. As result, dosage is reduced and foundry environment … Continued

Germinal 1604

Germinal 1604 is a high yield grain refining flux in tablet form. It is sodium free and contains high quantity of Titanium and Boron to allow a fine grain formation in the structure of Aluminium-Magnesium alloys. The product doesn’t have degassing action, therefore it is advisable to use degassing flux after the treatment with Germinal … Continued